RESUMEN
The advantages of microbial induced carbonate precipitation (MICP) as bio-cementation technology for tailings-solidification are under extensive investigation. In order to improve performance of bio-cementation, many strengthening materials were applied to the bio-cementation of tailings. Steel slag (SS) is a kind of industrial solid waste, its chemical composition and mineral composition are similar to cement, and it has a certain application prospect as an auxiliary cementing material. In this study, the properties and mechanism of SS strengthening MICP cementation of cyanide tailings (CT) were investigated. The results showed that Sporosarcina pasteurii growth is not inhibited by SS, and Sporosarcina pasteurii can promote the hydration reaction of SS, providing a suitable alkaline environment and Ca2+, promoting the production of more CaCO3 in the MICP process. When 200 mL of CT leachate was added 1.4 g SS (200-400 mesh), the adsorption of Cu, Pb, Zn, Cd, total cyanide (T-CN), and free cyanide (F-CN) reached 48.05%, 44.28%, 36.25%, 16.67%, 79.05%, and 67.20%, respectively. The maximum unconfined compressive strengthï¼UCSï¼ of the cemented body (with 5%, 150 mesh SS) was 1.97 MPa, which was 3.396 times as high as that without SS. The cemented body with the addition of SS (5%, 150 mesh) contained more carbonate bound Cu (2.75%), Pb (4.89%), Zn (5.37%), and Cd (5.75%), and less exchangeable Cu (3.65%), Pb (6.85%), Zn (2.27%), and Cd (4.42%) than that without SS. In summary, the addition of SS improved the UCS of cemented bodies and the stability of heavy metals and cyanide, reduced the environmental risks existing in the process of CT storage. Meanwhile, it also provides new ideas for resource utilization of industrial solid waste SS and improvement of mine filling materials.